The influence of chemical com position and structure on the machinability of high-chromium cast irons

Authors

  • V. V. Netrebko

Keywords:

Chemical composition, structure, influence.

Abstract

The influence of carbon and structure on the m achinability of high-chromium cast irons has been studied. With the increase of carbon content in cast iron the machinability becomes worse. When carbon content in cast iron was over 3 % , hypereutectic carbides had been formed, and they worsened the machinability abruptly. Compositions of cast irons for the parts which require mechanical treatment have been recommended.

References

Гарбер М.Е. Отливки из белых износостойких чугунов. М .: Машиностроение. 1972. 112с.

Ящерицын П.И . и др. Теория резания. Физические и тепловые процессы в технологических системах. Мн.: Выш . шк. 1990. 512с.

Герек А., Байка Л. Легированный чугун - конструкционный материал. М.: Мeталлургия. 1978. 208с.

Чейлях А.П. Экономнолегированные метастабильные сплавы и упрочняющие технологии. Харьков: ННЦХФТИ . 2003. 212с.

Belikov S., V olchok I., N etrebko V. Manganese influence on chromium distribution in high-chromium castiron // A rchives of Metallurgy and Materials Vol. 58. 3/2013. p.895-897

Цыпин И.И . Белые износостойкие чугуны. Структура и свойства. М .: Металлургия. 1983. 176с.

Волчок И .П ., Нетребко В.В. Влияние марганца на процессы структурообра-зования износостойкихвы сокохромистых чугунов // Строительство, материаловедение, машиностроение: Сб. науч. Трудов. Вып. 64. Дн-вск., П ГА - СА, 2012. с.301-304.

Гиршович Н.Г. К ристаллизация и свойства чугуна в отливках. М .-Л.: Машиностроение. 1966. 564с.

Published

2014-03-25

Issue

Section

Proceedings in memory of Starodubov