Influence of temperature annealing on the formation of special boundaries in armco-iron
Keywords:
Temperature effect, Armco-iron, coercive force, hardness, special boundaries in ferrite, grain size.Abstract
Purpose. Magnetic properties of Armco-iron with improved removal of impurities and in growing large grains, so you need to search for new modes of heat exposure. The study of special boundaries in the metal of ferritic single phase structure were carried out. Also determine the effect of specific boundaries and the grain size in the magnetic properties of ferrite in (coercive force Hc) Armco-iron. Methodology. We investigated the Armco-iron with a round rental diameter of 42 mm. The samples were heated at 900 degrees in the oven and heated 1, 2, 3 hours. Conducted research metallographic structure. Performed hardness, coercivity Hc and counting the number of special grain boundaries and size. Findings. It was established that the effects of temperature and different time of exposure varies coercive force Hc. With increasing temperature influence decreases the value of the coercive force Hc, hardness and grain size increases and the relative number of special boundaries in ferrite. Originality. Annealing low-metals and alloys results in increased specific boundaries in ferrite, reducing the size and increasing the coercivity magnetic permeability. Practical value. Materials with high number of special low-energy boundaries can compete with traditional metals in electrical and magnetism.
References
Большаков В.И., Сухомлин Г.Д. и др. Специальные границы в мартенситных структурах низкоуглеродистых сталей. // Металознавство та термічна обробка металив - 2006. - №4 (35) - С. 5 - 14. /
Bol'shakov V. I , Sukhomlin G.D. i dr. Spetsialnye granitsy v martensitnyh strukturah nizkouglerodistyh stalei. // Metaloznavstvo ta termichna obrobka metaliv - 2006. - №4. (35) - S. 5 - 14. http://ecat.diit.edu.ua
Лаборатория металлографии. / Панченко Е.В., Скаков Ю.А. и др. - М. Металлургия, 1965. - 440 с.
Laboratoriya metallografii. / Panchenko E.V.,Skakov i dr. - M. Metallurgiya, 1965. - 440 s. http://library.kpi.kharkov.ua/
Неразрушающий контроль: Справочник: В 8 т. / Под общ. Ред. В.В.Клюева. Кн. 1 В.В. Клюев, В.Ф. Мужицей, Э.С. Горкунов, В.Е. Щербинин. Магнитные методы контроля.-2е изд., испр.- М.: Машиностроение, 2006.-848с.
Nerazrushayuschiy kontrol: Spravochnik v 8 t. / Pod obsch. red. V.V. Klyueva. Kn.1 V.V. Klyuev, V.F. Muzhetsei, E.S. Gorkunov, V.E. Scherbinin. Magnitnye metody kontrolya. 2-e izd., ispr. - M.: Mashinostroenie, 2006.-848s. http://www.tdj.ru/index.php/news/40-2009-10-04-05-39-55/112
Салтыков С.А. Стереометрическая металлография. - М.: Мет-гия , 1970.-375 с. Saltykov S.A. Stereometricheskaya metallografiya. - M. Metallurgiya,1970. -375 s. http://www.twirpx.com/file/825320/
Сухомлин Г.Д. Специальные границы в феррите низкоуглеродистых сталей //Металлофизика и новейшие технологии. - 2013. Т. 35, № 9 - С.1237-1249.
Sukhomlin G.D. Spetsyalnye granitsy v ferrite nizkouglerodistyh stalei. //Metallofizika i noveishie tehnologii. - 2013. T. 36, № 9 - C.1237-1249. http://mars.arbicon.ru/?mdl=journal_info&idjoumal=981
Сухомлин Г.Д. Множественные специальные стыки границ зерен в ГЦК поликристаллах. //ФММ, т. 54, вып. 2.1982.- С. 402-405
Sukhomlin G.D. Mnozhestvennye spetsialnye ctyki granits zeren v GTSK polikristallah. //FMM, t. 54, vyp. 2. - 1982.- C. 402-405. http://fmm.imp.uran.ru/?raz=about
Bolshakov V., Sukhomlin G., Laukhin D., Beketov O., Derkach T., Kuksenko V. Special boundaries and plural grain boundary junctions in the hypoeutectoid ferrite of lowcarbon steels. // Theoretical foundations of civil engineering. - Warszawa.: Polit. Warsh. - 2007. - P. 73-80 https://architektura.um.warszawa.pl/
Downloads
Published
Issue
Section
License
Редакція Видання категорично засуджує прояви плагіату в статтях та вживає всіх можливих заходів для його недопущення. Плагіат розглядається як форма порушення авторських прав і наукової етики.
При виявлені у статті більш ніж 25% запозиченого тексту без відповідних посилань та використання лапок, стаття кваліфікується як така, що містить плагіат. У цьому випадку стаття більше не розглядається редакцією, а автор отримує перше попередження.
Автори, в статтях яких повторно виявлено плагіат, не зможуть публікуватися в усіх журналах Видавництва ДВНЗ «Придніпровська державна академія будівництва та архітектури».
Автори, які публікуються у цьому журналі, погоджуються з наступними умовами:
- Автори залишають за собою право на авторство своєї роботи та передають журналу право першої публікації цієї роботи на умовах ліцензії Creative Commons Attribution License, котра дозволяє іншим особам вільно розповсюджувати опубліковану роботу з обов'язковим посиланням на авторів оригінальної роботи та першу публікацію роботи у цьому журналі.
- Автори мають право укладати самостійні додаткові угоди щодо неексклюзивного розповсюдження роботи у тому вигляді, в якому вона була опублікована цим журналом (наприклад, розміщувати роботу в електронному сховищі установи або публікувати у складі монографії), за умови збереження посилання на першу публікацію роботи у цьому журналі.
- Політика журналу дозволяє і заохочує розміщення авторами в мережі Інтернет (наприклад, у сховищах установ або на особистих веб-сайтах) рукопису роботи, як до подання цього рукопису до редакції, так і під час його редакційного опрацювання, оскільки це сприяє виникненню продуктивної наукової дискусії та позитивно позначається на оперативності та динаміці цитування опублікованої роботи (див. The Effect of Open Access).