Structures, phase composition and properties formation of chromomanganse cast irons in the cast and normalization stay
Keywords:
chromomanganese cast iron, structure, properties, phase composition, normalization.Abstract
Annotation. Purpose. Study the structure and properties of chromo-manganese cast iron in the cast and normalized state. Methodology. The study objects in this work were the experimental-industrial melting chromomanganese cast iron samples Microstructure researches were carried out by using the optical microscope “Neophot-21”. Microhardness of phases and structural components was defined by using PМТ-3 by standard procedure. Phase composition of samples was studied by the diffractometer DRON–3М in FeК - radiation. Hardness of the investigated cast iron in the cast stay was determined by the Rockwell’s standard method. Findings.. Complex research were carried out and showed that the hardness of the investigated chrom-manganese cast iron is determined by the content of carbon, manganese and the number of carbide component. The maximum hardness in the cast and the normalized state characterized by alloys 2, 3, which allows to predict the increase of abrasive and shock-abrasive wear resistance in as cast and normalized condition. Originality. For chromomanganese cast irons the interrelation between the quantitative ratio of primary austenite dendrites and eutectic component in the cast and normalized state and properties (micromechanical characteristics and hardness). Practical value. Understanding the mechanisms of structural changes and to obtain quantitative laws describing the formation of structural components, enables you to control the structure and properties of the products from chromomanganese cast iron
References
Poddubniy A.N., Kulbovskiy I.K/, Dukov A.V. Mel`uchie shari s visokoy ekspluatacionoy stoikost`u is belogolegirovanogo chuguna [Grinding balls with high operational stability of white alloyed cast iron]. Casting production. – 1997. – P. 46
Sokolov O.G., Katzov K.B. Zhelzomargantzevie splavi [Ferromanganese alloys]. Kiev. Naukova dumka. – 1982. 212 p.
Materialy v mashinostroenii Spravochnik. – M. Mashinostroenie [Materials in mechanical engineering]. Reference guide M: machine building, P. 4, 1969. – 248 p.
Cheylax A.P., Klok D.V., Prekrasniy S.V. Razrabotka i issledovaniya ekonomnolegirovanix iznosostoikich chugunov s metastabilnoy strukturoy dlya bistroiznashivauchixsya detaley [Development and research of new economically alloyed wear-resistant cast iron with metastable structure of wearing parts]. Metal and casting of Ukraine. – 2006. – №5. – P. 13-17.
Samsonov G.V., Kosolapova T.Ya. Karbidi I splavi na ich osnove [Carbides and alloys on their basis Kiev. scientific thought]. Kiev. Naukova dumka. – 1976. P. 32-41.
Novikov N.V., Dub S.N., Bulichov S.I. Metodi ispitaniy na trechinostoykost` [Methods of mikrotests on crack resistance]. Plant laboratory. – 1988. – №7 – P. 60-67.
Kutsova V.Z., Kovzel M.A., Grebeneva A.V. Ratnicova I.V., Velichko O.O. Vliyanie legiryuchix elementov na formirovanie strukturi, fazovogo sostava i svoystv chromomarganzevogo chuguna v litom sostoyanii [The influence of alloying elements on the structure formation, phase composition and properties chromomagnetic cast iron in the cast state]. Metallurgical and mining industry. – 2015. - № 3 (294). – P. 45-48.
STRUCTURE, PHASE COMPOSITION AND PROPERTIES OF CHROMO-MANGANESE CAST IRON IN THE CAST STAY / V.Z. Kutsova, M.A. Kovzel, А.V. Grebeneva, O.O. Velichko, Z. Stradomski // New technologies and achievements in metallurgy, material engineering and production engineering. A collectivemonograph. - Czestochowa 2015. – №. 48. – P. 320 - 325.
Nesterenko A.M., Kutsova V.Z., Kovzel M.A. Issledovanie kristallicheskoy strukturi karbidov tipa Ме7С3 [The research of the carbides type as Ме7С3 crystal structure]. Metallophysic and new technologys. – 2003. - №1, P. 99-106.
Downloads
Published
Issue
Section
License
Редакція Видання категорично засуджує прояви плагіату в статтях та вживає всіх можливих заходів для його недопущення. Плагіат розглядається як форма порушення авторських прав і наукової етики.
При виявлені у статті більш ніж 25% запозиченого тексту без відповідних посилань та використання лапок, стаття кваліфікується як така, що містить плагіат. У цьому випадку стаття більше не розглядається редакцією, а автор отримує перше попередження.
Автори, в статтях яких повторно виявлено плагіат, не зможуть публікуватися в усіх журналах Видавництва ДВНЗ «Придніпровська державна академія будівництва та архітектури».
Автори, які публікуються у цьому журналі, погоджуються з наступними умовами:
- Автори залишають за собою право на авторство своєї роботи та передають журналу право першої публікації цієї роботи на умовах ліцензії Creative Commons Attribution License, котра дозволяє іншим особам вільно розповсюджувати опубліковану роботу з обов'язковим посиланням на авторів оригінальної роботи та першу публікацію роботи у цьому журналі.
- Автори мають право укладати самостійні додаткові угоди щодо неексклюзивного розповсюдження роботи у тому вигляді, в якому вона була опублікована цим журналом (наприклад, розміщувати роботу в електронному сховищі установи або публікувати у складі монографії), за умови збереження посилання на першу публікацію роботи у цьому журналі.
- Політика журналу дозволяє і заохочує розміщення авторами в мережі Інтернет (наприклад, у сховищах установ або на особистих веб-сайтах) рукопису роботи, як до подання цього рукопису до редакції, так і під час його редакційного опрацювання, оскільки це сприяє виникненню продуктивної наукової дискусії та позитивно позначається на оперативності та динаміці цитування опублікованої роботи (див. The Effect of Open Access).