Production equipment of cold deformed reinforcing hire with the wide range of consumer properties
Keywords:
reinforcing hire, bar, hank, hardening, production technology, consumer properties, cold deformation, strain aging, production lineAbstract
Purpose. Development based on the analysis of technological schemes for receiving the hardened reinforcing hire with use of hot and cold deformation and extension the list of requirements to consumer properties of this product technological line, providing production of cold deformed reinforcement with a periodic profile in hanks, classes of durability 500...600 MPa.Methodology. Comparable system analysis of technological solutions production lines for production of cold-rolled reinforcement, that consists in comparison with the requirements of new normative documents on properties of armature, and also the analysis of complex influence of the deformation-thermal affecting properties of of cold-rolled reinforcement. Findings. The new complex of equipment, that is logistic organized as a production line by allowing stably getting cold deformed reinforcement in the wide range of different properties is offered. Originality. For the first time offered the composition of technological equipment in the logistics flow line for hardenable cold deformation rebar, structural state which formed the optimal combination of active and cyclic deformations with subsequent high-speed bulk and surface heat, ensuring the flow of the entire volume of the product static-dynamic strain aging, and the small softening the surface layer state. Practical value. A line allows getting an armature conforming to the requirements of normative documents in combination with enhanceable: relaxation firmness, plasticity, corrosion resistance, fire resistance, resistance to cyclic loading and immunity to strain aging.
References
A. s. 433815 USSR, MKI S 21 D 1/18. Sposob termicheskoy obrabotki stalnyih izdeliy [The method of heattreatment of steel products]/ I.G.Hait, N.M.Mulin, E.A.Guzeev i dr. ; zayavl. 19.04.1968 ; opubl. 25.11.77, Byul. №43. (in Russian).
Babich V. K., Gul Yu. P., Dolzhenkov I. E. Deformatsionnoe starenie stali [Strain aging steel] //M.: Metallurgiya, 1972 – 320 p. (in Russian).
BS 4449:2005 Steel for the reinforcement of concrete — Weldable reinforcing steel — Bar, coil and decoiled product – Specification.
EN 10080:2005. Steel for the reinforcement of concrete. Weldable reinforcing steel. General.
DIN 4099-2:2003-08. Welding of reinforcing steel – Part 2: Quality assurance.
Vyisokoprochnaya armaturnaya stal [High-strength reinforcing steel] / Kugushin A.A., Uzlov I.G., Kalmyikov V.V., Madatyan S.A., Ivchenko A.V. – M.: Metallurgiya, 1986. – 272 p. (in Russian).
Gul Yu. P., Perchun G.I. Stabilizatsiya uprochnennogo sostoyaniya holodnodeformirovannoy nizkouglerodistoy stali [Stabilization of the state of cold-hardened carbon steel]// Metal Science and Heat Treatment. – 1992. - №2.- pp. 26-30. (in Russian).
Gul Yu. P. Vliyanie shemyi holodnoy deformatsii i rezhima stareniya na relaksatsionnuyu stoykost uprochnennoy malouglerodistoy stali [Effect of cold deformation schemes and modes of aging on the relaxation resistance hardened mild steel] / Yu. P. Gul; A. V. Ivchenko, M. Yu. Ambrazhey, S. V. Tischenko // Steel. –2011. – №10. – pp. 44-47. (in Russian).
Gul Yu.P., Ivchenko A.V., Ratushnyiy Yu.O. Sravnitelnoe issledovanie effektov staticheskogo deformatsionnogo stareniya nizkouglerodistoy stali pri razlichnyih shemah predvaritelnoy deformatsii [A comparative study of the effects of static strain aging of low carbon steel at various pre-distortion circuits] // Stroitelstvo, materialovedenie, mashinostroenie – [Сonstruction, materials science, mechanical engineering]. PDABA – Dnepropetrovsk: 2008, №46. – pp.23-31. (in Russian).
Gul Yu.P., Mironova O.Yu. Povyishenie konstruktivnoy prochnosti svarnyih konstruktsiy termomehanikotermicheskoy obrabotkoy (TMTO) [Increased structural strength of welded structures thermomechanics-heat treatment] // Proizvodstvo i primenenie termicheski uprochnennogo prokata v stroitelstve // sb. dokl. 11 Vsesoyuznoy konferentsii po dinamike osnovaniy, fundamentov i podzemnyih sooruzheniy. – Dnepropetrovsk. – 1988. – pp.114-118. (in Russian).
Gul Yu.P. Kompleksnaya intensifikatsiya sferoidiziruyuschego otzhiga nizkouglerodistyih staley dlya holodnoy vyisadki [Integrated intensification of spheroidizing annealing of low carbon steels for cold heading] / Yu.P. Gul, M.A. Sobolenko, A.V. Ivchenko // Steel. – 2012. – №6. – pp. 44-47. (in Russian).
Ivchenko A.V. Novyiy effektivnyiy armaturnyiy prokat v motkah klassa V500S dlya zhelezobetonnyih konstruktsiy [New effective reinforcing bars in coils B500C class for concrete structures] / Ivchenko A.V., Nedogibchenko A.I., Matyuhov S.A. i dr.// Beton i zhelezobeton v Ukraine – [Concrete and reinforced concrete in Ukraine]. - 2013. – №5. – pp.17-21.
Ivchenko A.V. Proizvodstvo armaturnogo prokata klassa V500S iz katanki povyishennoy prochnosti [The production of reinforcing bars of grade B500C from wire rod high strength] / A.V. Ivchenko, V.P. Kolpak, M.Yu. Ambrazhey dr. // Metizyi, –2006. – №03 (13). – pp. 40-43. (in Russian).
Ivchenko A.V., Ognesohrannost holodnodeformirovannogo armaturnogo prokata klassa V500S [The fire resistance of cold-deformed reinforcing bars of grade B500C]/ A.V. Ivchenko, Yu.P. Gul, R.V. Pankov, P.V. Kondratenko // Beton i zhelezobeton v Ukraine – [Concrete and reinforced concrete in Ukraine]. – 2015. – №5. – pp. 24-29. (in Russian).
Kolos S. N. Razrabotka tehnologii proizvodstva holodnodeformirovannoy armaturnoy stali po standartu ONORM B 4200 [Development of technology of production of cold-deformed reinforcing steel standard ONORM B 4200]/ Kolos S. N., Zinovenko A. V., Bondarenko V. I. // Metizyi. - 2009. - №1 (20). - pp.44-45. (in Russian).
Liniya dlya vygotovlennya armaturnogo prokatu [The line for the manufacture of reinforcing bar]: zayavka № ua201504119 v patentne vidomstvo Ukrayiny: MPK B21C 1/00, C21D 8/00 / Gul Yu.P., Dyiya H., Ivchenko A.V., Morgun M.P.; vlasn. NMetAU; zayavl. 28.04.2015. (in Ukrainian)
Liniya dlya vygotovlennya armaturnogo prokatu [The line for the manufacture of reinforcing bar]: zayavka № ua201511827 v patentne vidomstvo Ukrayiny: MPK B21C 1/00, C21D 8/00 / Gul Yu.P., Ivchenko O.V., Pankov R.V. ta insh.; vlasn. NMetAU; zayavl.30.11.2015. (in Ukrainian)
Madatyan S.A, Bondarenko V.I. Holodnaya deformatsiya. Perspektivyi holodnodeformirovannogo armaturnogo prokata [Cold deformation. The prospects of cold-deformed rebar]//Metallosnabzhenie i sbyit – [Metal supply and sales]. - 2007. – №4. – pp.50-53. (in Russian).
Interstate standard GOST «Prokat armaturnyiy dlya zhelezobetonnyih konstruktsiy. Tehnicheskie usloviya» [Rolled reinforcement for concrete structures. Specifications](The project, first edition) Available at: http://www.cstroy.ru/news/802/. (in Russian).
Mulin N.M. Termicheski uprochnennaya armatura povyishennoy nadezhnosti [Heat-strengthened rebar increased Ст р о ит е л ь ст в о , ма т ер и а л о в е д е н и е , ма ши но ст р о е н и е: Ст а р о д у б о в с к и е чт е н и я – 2 0 1 6reliability]/ Mulin N.M. , Hait I.G., Guzeev E.A. i dr. // Beton i zhelezobeton – [Concrete and reinforced concrete]. – 1972. – № 11. – pp. 20-24
Semenov A.A., Ivchenko A.V. Liniya dlya izgotovleniya holodnodeformirovannyih armaturnogo prokata periodicheskogo profilya v motkah [Production line for cold-deformed rebar periodic profile in coils]. Patent RF forThe utility model № 90719, kl. V21S 1/00, C 21. D 8/00, publ. 20.01.2010, BI №2, 2010 g. (in Russian).
Sposob izgotovleniya holodnodeformirovannoy armaturnoy provoloki [A method of manufacturing cold-deformed reinforcing wire]. Patent RF №2302916, kl. V21S 1/00, publ. 20.07.2007 g., BI №20, 2007 g. (in Russian).
Terin V. D. Vliyanie stepeni plasticheskoy deformatsii na svoystva holodnodeformirovannoy armaturyi [The influence of the degree of plastic deformation on the properties of cold-deformed rebar] / Terin V. D., Leshkevich O. N., Lenartovich D.V. // Sovershenstvovanie zhelezobetonnyih konstruktsiy, otsenka sostoyaniya i usilenie: Materialyi resp. nauch.-tehn. konferentsii / Pod. red. T.M. Petsolda.- Mn.: UP «Tehnoprint», 2001. – pp. 173-176.(in Russian).
Haritonov V.A. Problemyi i perspektivyi proizvodstva holodnodeformirovannoy armaturyi i izdeliy iz nee [Problems and prospects of production of cold-deformed armature and products] // Stroymetall. - 2010. - №3 (16). – pp.14-19. (in Russian).
Downloads
Published
Issue
Section
License
Редакція Видання категорично засуджує прояви плагіату в статтях та вживає всіх можливих заходів для його недопущення. Плагіат розглядається як форма порушення авторських прав і наукової етики.
При виявлені у статті більш ніж 25% запозиченого тексту без відповідних посилань та використання лапок, стаття кваліфікується як така, що містить плагіат. У цьому випадку стаття більше не розглядається редакцією, а автор отримує перше попередження.
Автори, в статтях яких повторно виявлено плагіат, не зможуть публікуватися в усіх журналах Видавництва ДВНЗ «Придніпровська державна академія будівництва та архітектури».
Автори, які публікуються у цьому журналі, погоджуються з наступними умовами:
- Автори залишають за собою право на авторство своєї роботи та передають журналу право першої публікації цієї роботи на умовах ліцензії Creative Commons Attribution License, котра дозволяє іншим особам вільно розповсюджувати опубліковану роботу з обов'язковим посиланням на авторів оригінальної роботи та першу публікацію роботи у цьому журналі.
- Автори мають право укладати самостійні додаткові угоди щодо неексклюзивного розповсюдження роботи у тому вигляді, в якому вона була опублікована цим журналом (наприклад, розміщувати роботу в електронному сховищі установи або публікувати у складі монографії), за умови збереження посилання на першу публікацію роботи у цьому журналі.
- Політика журналу дозволяє і заохочує розміщення авторами в мережі Інтернет (наприклад, у сховищах установ або на особистих веб-сайтах) рукопису роботи, як до подання цього рукопису до редакції, так і під час його редакційного опрацювання, оскільки це сприяє виникненню продуктивної наукової дискусії та позитивно позначається на оперативності та динаміці цитування опублікованої роботи (див. The Effect of Open Access).